ICP-OES/ICP-MS技术研究枯矾及其伪品的差异特征元素及无机元素含量分布

刘圣金; 乔婷婷; 马瑜璐; 房方; 林瑞超; 包敏婕; 陈瑶; 吴德康

doi:10.13422/j.cnki.syfjx.20190511

您当前的位置：

首页 >

文章列表页 >

ICP-OES/ICP-MS技术研究枯矾及其伪品的差异特征元素及无机元素含量分布

矿物药研究专题 | 更新时间：2021-02-09

- ICP-OES/ICP-MS技术研究枯矾及其伪品的差异特征元素及无机元素含量分布
- Research on Differential Feature Elements and Characteristic Spectrum of Inorganic Elements Between Calcined Alumen and Its Counterfeit Processed Products Based on ICP-OES/ICP-MS
- 中国实验方剂学杂志 2019年25卷第5期页码：1-7
- 作者机构：
  
  1.南京中医药大学　江苏省中药资源产业化过程协同创新中心，中药资源产业化与方剂创新药物国家地方联合工程研究中心，国家中医药管理局中药资源循环利用重点研究室，江苏省中药功效物质重点实验室，南京　 210023；
  2.北京中医药大学，北京　 100029
- 作者简介：
  
  刘圣金，博士，副教授，从事中药鉴定、质量标准及矿物药研究，Tel：025-85811511，E-mail: 13770653305@139.com
  吴德康，教授，从事中药鉴定、质量标准及矿物药研究，Tel：025-85811511，E-mail: wudekang2008@126.com
- 基金信息：
  
  2017年中医药公共卫生服务补助专项“全国中药资源普查项目”(财社〔2017〕66号);江苏高校品牌专业建设工程项目(PPZY2015A070);中医药行业专项(2015468004-2-1);国家自然科学基金项目(81673566;81573556)
- DOI：10.13422/j.cnki.syfjx.20190511
  中图分类号： R284.1;R22;R2-03;R289
- 收稿日期：2018-04-06，
  
  网络出版日期：2018-11-21，
  
  纸质出版日期：2019-03-05
- 稿件说明：
移动端阅览
刘圣金, 乔婷婷, 马瑜璐, 等. ICP-OES/ICP-MS技术研究枯矾及其伪品的差异特征元素及无机元素含量分布[J]. 中国实验方剂学杂志, 2019,25(5):1-7.

Sheng-jin LIU, Ting-ting QIAO, Yu-lu MA, et al. Research on Differential Feature Elements and Characteristic Spectrum of Inorganic Elements Between Calcined Alumen and Its Counterfeit Processed Products Based on ICP-OES/ICP-MS[J]. Chinese journal of experimental traditional medical formulae, 2019, 25(5): 1-7.
刘圣金, 乔婷婷, 马瑜璐, 等. ICP-OES/ICP-MS技术研究枯矾及其伪品的差异特征元素及无机元素含量分布[J]. 中国实验方剂学杂志, 2019,25(5):1-7. DOI： 10.13422/j.cnki.syfjx.20190511.

Sheng-jin LIU, Ting-ting QIAO, Yu-lu MA, et al. Research on Differential Feature Elements and Characteristic Spectrum of Inorganic Elements Between Calcined Alumen and Its Counterfeit Processed Products Based on ICP-OES/ICP-MS[J]. Chinese journal of experimental traditional medical formulae, 2019, 25(5): 1-7. DOI： 10.13422/j.cnki.syfjx.20190511.

摘要

目的：

分析临床用枯矾及其伪品铵明矾炮制品的差异无机元素，并建立其特征图谱，为枯矾提供新的质量控制手段。

方法：

应用ICP-OES及ICP-MS测定枯矾和铵明矾炮制品中22种无机元素的含量，采用SPSS 16.0软件对原始数据进行分层聚类分析，以SIMCA-P 13.0软件配合

检验及秩和检验对差异性无机元素进行识别，建立枯矾与伪品的无机元素特征谱。

结果：

枯矾中主含K

Al等元素，伪品主含Al

Fe等元素；枯矾Cr

Mn含量相对较高，铵明矾炮制品Mn

Ga含量相对较高。其中枯矾中K元素含量约为伪品的205倍；相反，Fe

Ga等元素，伪品的平均含量远高于枯矾，分别约为枯矾平均含量的33，46，38，27倍。聚类分析将18个样品聚类为枯矾和铵明矾炮制品两大类。共筛选出18种含量具有显著性差异(

0.05)的元素，分别为Be

Pb。建立了枯矾、伪品枯矾含21种无机元素特征谱。

结论：

该分析方法可用于枯矾的质量控制。

Abstract

Objective:

To provide the new quality control means for Alumen by investigating the elemental differences between calcined Alumen and its counterfeit processed products of ammonium alum

and establishing their characteristic chromatogram.

Method:

The contents of 22 inorganic elements both in calcined Alumen and processed products of ammonium alum were determined by means of inductively coupled plasma (ICP)-optical emission spectrometer-mass spectrometry (ICP-OES/ICP-MS)

SPSS 16.0 was used for cluster analysis (CA) while SIMCA-P 13.0 with

-test and Rank-Sum test was used to identify the differential inorganic elements. In addition

the characteristic spectrum of the inorganic elements for calcined Alumen and counterfeit calcined alumen were established.

Result:

Calcined Alumen had highest contents of K and Al while counterfeit calcined Alumen has highest contents of Al and Fe; Cr

and Mn contents in calcined Alumen were relatively higher

while Mn

and Ga contents in processed products of ammonium alum were relatively higher. The content of K in calcined Alumen was about 205 times of that of counterfeit products. On the contrary

the average contents of Fe

Mn and Ga in counterfeit products of ammonium alum were much higher than those in calcined Alumen

27 times

respectively. A total of 18 samples were clustered into two categories in CA: calcined Alumen and processed products of ammonium alum. 18 inorganic elements showed significant difference in contents(

0.05)

and Pb respectively. Characteristic spectrum of 21 inorganic elements in calcined Alumen and counterfeit calcined Alumen were established.

Conclusion:

This method can be used for quality control of calcined Alumen.

关键词

Keywords

references

国家药典委员会．中华人民共和国药典．一部 [M]. 北京：中国医药科技出版社， 2015 ： 108 .

韩效钊，王雄，陈敏，等．利用矾泥制备铵明矾 [J]. 化工环保， 2002 , 22 ( 5 ): 280 - 283 .

赵剑宇，田凯．微波酸化法从高岭土制取铵明矾的研究 [J]. 无机盐工业， 2006 , 38 ( 9 ): 32 - 34 .

徐耀兵，王勤辉，施正伦，等．含钒灰渣酸浸液结晶铵明矾的工艺条件 [J]. 过程工程学报， 2009 , 9 ( 5 ): 927 - 931 .

黄燕华，王建浩，姚志远，等．结晶法由硫辛酸厂含铝废水制备铵明矾 [J]. 过程工程学报， 2013 , 13 ( 3 ): 436 - 441 .

林瑞超．矿物药检测技术与质量控制 [M]. 北京：科学出版社， 2013 ： 693 .

乔婷婷，刘圣金，林瑞超，等．基于ICP-OES/MS技术的白矾及其伪品铵明矾的无机元素差异性分析 [J]. 中药材， 2016 , 39 ( 11 ): 2462 - 2468 .

尤淑霞．白矾及炮制品品质评价研究 [D]．南京：南京中医药大学， 2011 .

刘圣金，吴德康，林瑞超，等．矿物药青礞石无机元素的ICP-MS分析 [J]. 药物分析杂志， 2010 , 30 ( 11 ): 2067 - 2074 .

李冰，杨红霞．电感耦合等离子体质谱原理和应用 [M]. 北京：地质出版社， 2005 ： 104 .

刘圣金，杨欢，林瑞超，等．矿物药禹余粮微波消解/ICP-AES无机元素分析及综合评价 [J]. 中国现代中药， 2015 , 17 ( 9 ): 899 - 904 .

刘圣金，吴德康，林瑞超，等．矿物药青礞石、煅青礞石无机元素的ICP-MS分析 [J]. 中国药房， 2011 , 22 ( 19 ): 1777 - 1780 .

LIU S J , YANG H , WU D K , et al . Analysis of inorganic elements inmineral Chinese medicine Limonitum after processing [J]. Lat Am J Pharm , 2014 , 33 ( 8 ): 1245 - 1251 .

刘圣金．矿物药青礞石质量控制技术研究 [D]．南京：南京中医药大学， 2012 .

JIA X Y , GONG D R , ZHAO J Y , et al . Zwitterion-functionalized polymer microspheres as a sorbent for solid phase extraction of trace levels of V(V)，Cr(Ⅲ)，As(Ⅲ)，Sn(Ⅳ)，Sb(Ⅲ) and Hg(Ⅱ) prior to their determination by ICP-MS [J]. Mikrochim Acta , 2018 , 185 ( 4 ): 228 .

刘洋，郭美玲，杜雪，等 . ICP-MS测定10种药材中8种无机元素的含量及其统计分析 [J]. 中国实验方剂学杂志， 2018 , 24 ( 20 ): 38 - 44 .

杨月，陈艳姣，张爱琛，等 . 土壤无机元素含量与三七药材品质的关系 [J]. 中国实验方剂学杂志， 2018 , 24 ( 13 ): 47 - 53 .

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

矿物药白矾、枯矾及其伪品的SEM, XRD鉴别分析

无机元素特征谱结合化学计量学鉴别黄芩的生长年限

不同矿物成因禹余粮质量评价及优质矿产资源筛选

基于ICP-MS对不同产地藠头无机元素的主成分分析和聚类分析

蒲公英酚类特征成分含量测定及其特征图谱质量表征关联分析